Aluminum Angle Bar

The advantages of aluminum alloy are lightweight, excellent electrical and thermal conductivity, high corrosion resistance and ductility.

Aluminum alloy is soft and usually alloyed with copper, zinc, magnesium, silicon, manganese and lithium to increase strength. When aluminum alloy is exposed to air, an anti-oxidant coating will be formed instantly to protect products. Aluminum alloy is one of the lightest metals. The application of products ranges from precision technology to daily commodities.

Mechanical Properties

  • Tensile Strength, Ultimate
  • 120 ~ 420 Mpa
  • Tensile Strength, Yield
  • 60 ~ 300 Mpa
  • Hardness, Brinell
  • 40 ~ 108

Product Specification and Size :

Standard Specification: GB/T 6892, ASTM B221, EN754, EN 755

Alloy and Temper
Alloy Temper
5xxx: 5083 O, H112
6xxx: 6005, 6060, 6061, 6063, 6082,6463 T5, T6, T66

Alloy Designation (For Reference)

Comparison of Alloy Designations for Aluminum Products

Alloy Series Chinese Standard American Standard European Standard
5xxx Series 5083 5083 EN AW-5083
6xxx Series 6005 6005  
6060 6060 EN AW-6060
6061 6061 EN AW-6061
6063 6063 EN AW-6063
6082 6082 EN AW-6082
6463 6463 EN AW-6463

Temper Designation (For Reference)

Temper Definition
O Annealed
H112 Slightly strain harden from working at an elevated temperature or from limited amount of cold work
T5 Cooled from an elevated temperature shaping process and then artificially aged
T6 Solution heat-treated and then artificially aged
T66 Solution heat-treated and then artificially aged - mechanical property level higher than T6 achieved through special control of the process (6000 series alloys)

Available Size Range

Dimension Range
A 10mm~200mm
B 10mm~200mm
T 2mm~15mm
Length 1,000~6,000mm

Application

Aluminum angles are used in numerous industrial applications, including scaffolding, shipbuilding, transmission towers and furniture applications.

- Production Process: Extruded
- Form & Image: Equal Angle, Unequal Angle
- Surface Finish: Mill Finish, unless otherwise specified
- Surface Protection: Paper interleaved

Chemical Composition

Alloy Si Fe Cu Mn Mg Cr Zn Ti Others:
Each		 Others:
Total		 Al: Min.
5083 0.40 0.40 0.10 0.40~1.0 4.0~4.90 0.05~0.25 0.25 0.15 0.05 0.15 remainder
6060 0.30~0.60 0.10~0.30 0.10 0.10 0.35~0.60 0.05 0.15 0.10 0.05 0.15 remainder
6061 0.40~0.80 0.70 0.15~0.40 0.15 0.80~1.20 0.04~0.35 0.25 0.15 0.05 0.15 remainder
6063 0.20~0.60 0.35 0.10 0.10 0.45~0.90 0.10 0.10 0.10 0.05 0.15 remainder
6082 0.70~1.30 0.50 0.10 0.40~1.0 0.60~1.20 0.25 0.20 0.10 0.05 0.15 remainder
6463 0.20~0.60 0.15 0.20 0.05 0.45~0.90 - 0.05 - 0.05 0.15 remainder